抗靜電ABS流動性高的有哪些？
無色產(chǎn)品在攝氏 23 度時的典型值測試方法單位數(shù)值
2 - 4
屬性:ABS 德國朗盛Novodur P2H-AT 抗靜電.高光澤.抗撞擊.流動性好
流變性能
Melt Volume Rate 220 °C/10 Kg
ISO 1133
cm3/10min
37
Melt Volume Rate, 200 °C/21,6 Kg MVR
ISO 1133
cm3/10mi
-
機械性能
Impact Strength, Notched Izod, 4mm bar, 0.25mm Notch Radius, 23 °C
ISO 180
J/m
-
Impact Strength, Notched Izod, 4mm bar, 0.25mm Notch Radius, -30 °C
ISO 180
J/m
-
Charpy Notched, 23° C
ISO 179
kJ/m2
16
Charpy Notched, -30° C
ISO 179
kJ/m2
7
Charpy Unnotched, 23° C
ISO 179
kJ/m2
100
Charpy Unnotched, -30° C
ISO 179
kJ/m2
80
Tensile stress at yield, 23° C
ISO 527
MPa
44
Tensile strain at yield, 23° C
ISO 527
%
2.1
Tensile strain at break, 23° C
ISO 527
%
*
Tensile Modulus
ISO 527
MPa
2500
Tensile Creep Modulus (1000h)
ISO 899
MPa
1500
Tensile Creep Modulus (1h)
ISO 899
MPa
2200
Elongation at Break (MD)
%
-
Elongation at Break (TD)
%
-
Flexural Strength
ISO 178
MPa
-
Flexural Modulus
ISO 178
MPa
-
Hardness, Shore D
ISO 868
-
Hardness, Shore A
ISO 868
-
Puncture, Total Energy
J
-
Ball Indentation hardness H
ISO 2039-1
MPa
-
熱性能
Vicat Softening Temperature
ISO 306
°C
98
Vicat Softening Temperature, B/1 (120°C/h, 10N)
ISO 306
°C
-
Vicat Softening Temperature, A/2 (50°C/h, 50N)
ISO 306
°C
-
Heat Deflection Temperature; (annealed) method Af, 1.8 MPa
ISO 75
°C
93
Heat Deflection Temperature; (annealed) method Bf, 0.45 MPa
ISO 75
°C
97
Coefficient of Linear Thermal Expansion
ISO 11359
10-6/°C
90
Thermal conductivity
DIN 52612-1
W/(m K)
-
其他屬性
Specular gloss, 60°
%
93
Density
ISO 1183
kg/m3
1050
Oxygen Transmission Rate (23°C/0% RH)
cc/m2/day
-
Filler content (% Ash)
%
電氣性能
Dielectric Constant (100 Hz)
IEC 60250
-
3
Dissipation Factor (100 Hz)
IEC 60250
-
55
Dissipation Factor (1 MHz)
IEC 60250
-
90
Volume Resistivity
IEC 60093
Ohm*m
>1E13
Surface Resistivity
IEC 60093
Ohm
>1E15
Processing (Melt) Temperature
ISO 294
°C
220 - 260
Mold Temperature
ISO 294
°C
70
Injection velocity
ISO 294
mm/s
240
Drying Temperature
°C
80
Drying Time
hr