| 詳細(xì)介紹： |
| STOODY產(chǎn)品系列 |
| STICK(SMAW)堆焊手工焊條 | ||||
產(chǎn)品
|
直徑(mm)
|
成份
|
強(qiáng)度KSI
|
硬度 HRC
|
19
|
3.2/4.0/4.8/6.4
|
26.0%C Mn Si Cr Mo
|
錳鋼二層45-49
中碳鋼二層51-55 |
|
31
|
3.2/4.0/4.8/6.4 |
34.0%C Mn Si Cr Mo
|
錳鋼二層47-49
碳鋼二層45-48 |
|
35
|
3.2/4.0/4.8/6.4
|
38.0%C Mn Si Cr
|
錳鋼二層50-53
加硬達(dá)到58-60 |
|
45
|
4.0
|
48.0%C Mn Si Cr Mo V Ti
|
59-61
|
|
77
|
3.2/4.0/4.8/6.4
|
24.0%C Mn Si Cr Mo
|
錳鋼二層42-50
碳鋼二層49-54 |
|
1102
|
3.2/4.0
|
10.7%C Mn Si Cr Ni
|
52-68
|
|
1105
|
3.2/4.0/4.8/6.4
|
5.00%C Mn Si Cr Mo V
|
1045鋼二層38-42
|
|
2110
|
3.2/4.0/4.8/6.4
|
31.0%C Mn Si Cr Ni
|
T.S.119 Y.S.76.4 EL40%
|
錳鋼二層
加硬達(dá)到50-55 |
2134
|
4.0/4.8/6.4
|
36.0%C Mn Si Cr Mo
|
錳鋼二層45-50
1045板二層56-60 |
|
BUILD UP LH
|
3.2/4.0/4.8/6.4
|
4.50%C Mn Si Cr Mo
|
T.S.118 Y.S.113
EL6% |
中碳鋼一層27
中碳鋼三層31 |
DYNAMANG |
3.2/4.0/4.8/6.4/8.0
|
21.0%C Mn Si Cr Ni
|
T.S.l20 Y.S.70
EL42% |
錳鋼一層180BHN
加硬達(dá)到500BHN |
RAILEND932
|
4.0/4.8/6.4
|
6.00%C Mn Si Cr Mo
|
T.S.150
|
38-40
|
SELF HARDENING
|
3.2/4.0/4.8/6.4
|
12.0%C Mn Si Cr Ni
|
52-58
|
|
SUPERCHROME
|
3.2/4.0/4.8/6.4
|
38.0%C Mn Si Cr
|
錳鋼二層54-61
碳鋼二層58-63 |
|
 |