| Grade : | 1.4419耐腐蝕鋼片/板和帶材 | |||||
| Number: | X38CrMo14 | |||||
| Classification: | 馬氏體不銹鋼 | |||||
| Density: | 7.7 g/cm 3 | |||||
| Standard: | ||||||
| EN 10088-2:2005不銹鋼。通用耐腐蝕鋼片/板和帶材交貨技術(shù)條件 | ||||||
| EN 10088-3:2005不銹鋼。一般用途耐腐蝕鋼的半成品、棒材、線材、型材和光亮產(chǎn)品的交貨技術(shù)條件 | ||||||
| EN 10088-1:2005不銹鋼。不銹鋼清單 | ||||||
| Equivalent grades: | ||||||
| Chemical comb % of steel X38CrMo14 (1.4419): EN 10088-2-2005 | ||||||
| 在詢問和訂購時(shí)可能會商定更嚴(yán)格的碳排放范圍 | ||||||
| 硫含量的特定范圍可以提供特定性能的改善。對于可加工性，建議并允許將硫含量控制在0.015%至0.030%之間。對于可焊性，建議并允許將硫含量控制在0.008%至0.030%之間。對于可極化性，建議將硫含量控制在最大0.015%。 | ||||||
| 未經(jīng)買方同意，不得故意將本表中未列出的元素添加到鋼材中，除非對鑄件進(jìn)行精加工 | ||||||
| C | Si | Mn | P | S | Cr | Mo |
| 0.36 - 0.42 | max 1 | max 1 | max 0.04 | max 0.015 | 13 - 14.5 | 0.6 - 1 |
| Mechanical properties of steel X38CrMo14 (1.4419) | ||||||
| Rm - Tensile strength (MPa) (+A) | 760 | |||||
| A - Min. elongation at fracture (%) (+A) | 15 | |||||
| Brinell hardness (HB): (+A) | 235 | |||||
|