| PMMA VR-L40 三菱麗陽株式會社 物性數(shù)據(jù) |
| 規(guī)格級別： | --- | 外觀顏色： | --- |
| 用途概述： | --- | ||
| 備注說明： | 耐沖擊材料 | ||
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.16 | --- |
| 全光線透射系數(shù) | 3.2mm | ASTM D-1003 | 92 | % | |
| 折射率 | --- | ASTM D-542 | 1.49 | nd | |
| 吸水率 | 24hr | ASTM D-570 | 0.4 | % | |
| 成形收縮率 | --- | ASTM D-955 | 0.3-0.7 | % | |
| 機械性能 | 抗拉強度 | ASTM NO.1 | ASTM D-638 | 430 | Kg/cm2 |
| 延展率 | ASTM NO.1 | ASTM D-638 | 80 | % | |
| 抗彎強度 | 1/4"棒 | ASTM D-790 | 630 | Kg/cm2 | |
| 彎曲彈性模量 | 1/4"棒 | ASTM D-790 | 2.0×104 | Kg/cm2 | |
| 懸臂梁式?jīng)_擊強度 | 1/4"付 | ASTM D-256 | 11 | kg.cm/cm | |
| 洛氏硬度 | M scale | ASTM D-785 | 67 | --- | |
| 電氣性能 | 表面電阻系數(shù) | --- | JIS K-6911 | >1016 | Ω |
| 體積電阻系數(shù) | --- | JIS K-6911 | >1015 | Ω.m | |
| 絕緣擊穿強度 | --- | JIS K-6911 | 15 | kv/mm | |
| 介電常數(shù) | 60Hz | JIS K-6911 | 3.9 | 60HZ | |
| 介質(zhì)損耗角正切 | 60HZ | JIS K-6911 | 0.04 | --- | |
| 耐電弧性 | --- | JIS K-6911 | 沒有痕跡 | --- | |
| 熱 性 能 | 維卡軟化溫度 | 1kg | ASTM D-1525 | 109 | °C |
| 熔體流動性 | 230°C 3.8kg | ASTM D-1238 | 2.2 | g/10min | |
| 比熱 | --- | --- | 0.35 | cal/g/°C | |
| 線膨脹系數(shù) | --- | ASTM D-696 | 9×10-5 | cm/cm/℃ | |
| 熱傳導系數(shù) | --- | ASTM C-177 | 5×10-4 | cal/s/cm/°C | |
| 載荷撓曲溫度 | 18.56kg/cm2 | ASTM D-648 | 94 | °C | |