| 熔體流動(dòng)速率 (200℃×5kgf(49N)) | 2.1 | g/10min | ASTM D-1238(ISO 1133) |
| 比重 (23℃/23℃) | 1.07 | ASTM D-792(ISO 1183) | |
| 熔體流動(dòng)速率 (220℃×10kgf(98N)) | 26 | g/10min | ASTM D-1238(ISO 1133) |
| 彎曲強(qiáng)度 (23℃) | 730(72) | kg/cm(MPa) | ASTM D-790(ISO 178) |
| IZOD沖擊強(qiáng)度 (23℃1/4"厚) | 15(147) | kg.cm/cm(J/m) | ASTM D-256(ISO R180) |
| 洛氏硬度 (23℃) | R-105 | ASTM D-785(ISO 2039/2) | |
| 拉伸強(qiáng)度 (23℃) | 450(44) | kg/cm(MPa) | ASTM D-638(ISO 527) |
| 彎曲模量 (23℃) | 22000(2160) | kg/cm(MPa) | ASTM D-790(ISO 178) |
| 燃燒性 (FILE NO E162823) | 1/16"HB All Corlor | UL 94 | |
| 維卡軟化點(diǎn) (1Kg load) | 102 | ℃ | ASTM D-1525(ISO 306) |
| 熱變形溫度 | |||
| (Unanneaied 18.6kg/cm2(1/2"厚)) | 87 | ℃ | ASTM D-648(ISO 75/A) |
| (Annealed(8℃×8hr)) | 99 | ℃ | ASTM D-1238(ISO 1133) |