| 熔體流動速率 | |||
| (200℃×5kgf(49N)) | 1.6 | g/10min | ASTM D-1238(ISO 1133) |
| (220℃×10kgf(98N)) | 17 | g/10min | ASTM D-648(ISO 75/A) |
| 比重 (23℃) | 1.05 | ASTM D-792(ISO 1183) |
| 抗張強度 (23℃) | 510(50) | kg/cm(MPa) | ASTM D-638(ISO 527) |
| 彎曲模數(shù) (23℃) | 27000(2650) | kg/cm(MPa) | ASTM D-790(ISO 178) |
| 彎曲強度 (23℃) | 850(84) | kg/cm(MPa) | ASTM D-790(ISO 178) |
| IZOD沖擊強度 (23℃) | 20(196) | kg.cm/cm(J/m) | ASTM D-256(ISO R180) |
| 洛式硬度 (23℃) | R-110 | ASTM D-785(ISO 2039/2) |
| 熱變形溫度 (Unanneaied 18.6kg/cm2(1/2"厚)) | 89 | ℃ | ASTM D-648(ISO 75/A) |
| 燃燒性 (FILE NO.E162823) | 1/16"HB All Color | UL 94 | |
| 維卡軟化點 (1Kg load) | 104 | ℃ | ASTM D-1525(ISO 306) |
| 熱變形溫度 (Annealed(8℃×8hr)) | 101 | ℃ | ASTM D-648(ISO 75/A) |