| 熔體流動速率 (220℃×10kg) | 50 | g/10min | ASTM D-1238 |
| 比重 | 1.05 | 23/23℃ | ASTM D-792 |
| 熔體流動速率 (200℃×5kg) | 4.5 | g/10min | ASTM D-1238 |
| 引張強(qiáng)度 | 470 | kg/cm | ASTM D-638 |
| 洛氏硬度 | 115 | R | ASTM D-785 |
| 伸長率 | 20 | % | ASTM D-638 |
| 彎曲彈性率 | 3.7×10 | lb/in | ASTM D-790 |
| IZOD沖擊強(qiáng)度 (1/8") | 17 | kg.cm/cm | ASTM D-256 |
| 彎曲彈性率 | 2.6×10 | kg/cm | ASTM D-790 |
| 彎曲強(qiáng)度 | ASTM D-790 | ||
| 10770 | lb/in | ||
| 760 | kg/cm | ||
| IZOD沖擊強(qiáng)度 (1/4") | 15 | kg.cm/cm | ASTM D-256 |
| 引張強(qiáng)度 | 6540 | lb/in | ASTM D-638 |
| IZOD沖擊強(qiáng)度 | ASTM D-256 | ||
| (1/8") | 3.2 | ft.lb/in | |
| (1/4") | 2.8 | ft.lb/in |
| 熱變形溫度 | ASTM D-648 | ||
| 89(192) | ℉ | ||
| 99(210) | ℃ | ||
| 維卡軟化點(diǎn) | 221 | ℉ | ASTM D-1525 |
| 燃燒性 (File No. E56070 UL&C-UL) | 1/16"HB | ||
| 維卡軟化點(diǎn) | 105 | ℃ | ASTM D-1525 |