| 熔體流動(dòng)速率 (220℃×10kg) | 7.5 | g/10min | ASTM D-1238 |
| 比重 | 1.03 | 23/23℃ | ASTM D-792 |
| 熔體流動(dòng)速率 (200℃×5kg) | 0.7 | g/10min | ASTM D-1238 |
| 彎曲強(qiáng)度 | 620 | Kg/cm | ASTM D-790 |
| IZOD沖擊強(qiáng)度 (1/4") | 6.5 | ft.lb/in | ASTM D-256 |
| 洛氏硬度 | 102 | R | ASTM D-785 |
| 引張強(qiáng)度 | 5530 | lb/in | ASTM D-638 |
| IZOD沖擊強(qiáng)度 (1/8") | 40 | kg.cm/cm | ASTM D-256 |
| 彎曲強(qiáng)度 | 8800 | lb/in | ASTM D-790 |
| 彎曲彈性率 | 3.0×105 | lb/in | ASTM D-790 |
| 引張強(qiáng)度 | 390 | Kg/cm | ASTM D-638 |
| 彎曲彈性率 | 2.1×104 | Kg/cm | ASTM D-790 |
| 伸長(zhǎng)率 | 40 | % | ASTM D-638 |
| IZOD沖擊強(qiáng)度 | ASTM D-256 | ||
| (1/4") | 35 | kg.cm/cm | |
| (1/8") | 7.5 | ft.lb/in |
| 維卡軟化點(diǎn) | 103 | ℃ | ASTM D-1525 |
| 熱變形溫度 | 87(189) | ℉ | ASTM D-648 |
| 燃燒性 (File No. E56070 UL&C-UL) | - | 1/16"HB | |
| 維卡軟化點(diǎn) | 217 | ℉ | ASTM D-1525 |
| 熱變形溫度 | 97(206) | ℃ | ASTM D-648 |