產(chǎn)品參數(shù)
| 性能項目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.32 | ||
| 機(jī)械性能 | 彎曲強(qiáng)度 | ASTM D-790 | 6700 | psi | |
| 彎曲模量 | ASTM D-256 | 0.6 | ft.lb/in | ||
| 彎曲模量 | ASTM D-790 | 33000 | KJ/m2 | ||
| 彎曲強(qiáng)度 | ASTM D-790 | 470 | Kg/cm2 | ||
| 彎曲強(qiáng)度 | ASTM D-790 | 46 | MPa | ||
| Izod缺口沖擊強(qiáng)度 | ASTM D-256 | 3 | Kg.cm/cm | ||
| 拉伸屈服強(qiáng)度 | ASTM D-638 | 29 | MPa | ||
| 彎曲模量 | ASTM 790 | 3240 | MPa | ||
| 拉伸屈服強(qiáng)度 | ASTM D-638 | 300 | Kg/cm2 | ||
| 斷裂伸長率 | ASTM D-638 | 20 | % | ||
| 拉伸屈服強(qiáng)度 | ASTM D-638 | 4300 | psi | ||
| 彎曲模量 | ASTM D-790 | 470 | psi | ||
| 彎曲模量 | ASTM D-256 | 30 | J/m | ||
| 熱性能 | 熱變形溫度 | 1.82Mpa | ASTM D-648 | 95 | ℃ |
| 耐燃性 | ASTM D-UL94 | V-0 | class | ||
| 熱變形溫度 | 1.82Mpa | ASTM D-648 | 205 | °F | |