產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.9 | g/cm3 | |
| 熔體流動(dòng)速率 | 230℃/2.16 kg | ASTM D1238 | 8.0 | g/10 min | |
| 機(jī)械性能 | 洛氏硬度 | ASTM D785 | 84 | ||
| 抗張強(qiáng)度 | 屈服 | ASTM D638 | 26.5 | MPa | |
| 斷裂伸長(zhǎng)率 | ASTM D638 | >500 | % | ||
| 彎曲模量 | ASTM D790 | 785 | MPa | ||
| 無(wú)缺口懸臂梁沖擊 | 23℃ | ASTM D256 | 49.0 | J/m | |
| 熱性能 | 熱變形溫度 | 0.45 MPa, 未退火 | ASTM D648 | 90.0 | ℃ |
| 維卡軟化點(diǎn) | ASTM D1525 3 | 135 | ℃ | ||
| 其它 | 光滑面 | 45° | ASTM D2457 | 120 | |
| 混濁 | ASTM D1003 | 1.2 | % | ||
| 薄膜厚度 | 30 | μm | |||
| 抗張強(qiáng)度 | MD: 斷裂 | ASTM D882 | 44.1 | MPa | |
| TD: 斷裂 | ASTM D882 | 34.3 | MPa | ||
| 伸長(zhǎng)率 | MD: 斷裂 | ASTM D882 | 600 | % | |
| TD: 斷裂 | ASTM D882 | 700 | % | ||