產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動(dòng)速率 | 230℃,2.16kg | ASTM D-1238 | 7 | g/10min |
| 比重 | ASTM D-792 | 1.13 | |||
| 成型收縮率 | 2mm(t) | SGC Method | 0.2-0.9 | % | |
| 機(jī)械性能 | 屈服拉伸強(qiáng)度 | 50mm/min | ASTM D-638 | 109 | MPa |
| 斷裂伸長(zhǎng)率 | 50mm/min | ASTM D-638 | 3 | % | |
| 彎曲強(qiáng)度 | ASTM D-747 | 147 | MPa | ||
| 彎曲模量 | ASTM D-790 | 5884 | MPa | ||
| Izod沖擊強(qiáng)度 | 23℃ | ASTM D-256 | 13 | kg·cm/cm | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 115 | R scale | |
| 熱性能 | 熱變形溫度 | 4.6kg/cm2(1/4”) | ASTM D-648 | 163 | ℃ |
| 阻燃性 | 1/8" | UL 94 | HB | ||
| 阻燃性 | 1/16" | UL 94 | HB | ||