| 熔體流動速率 (230℃ 2.16kg) | 10 | g/10min | ASTM D-1238 |
| 比重 | 0.93 | ASTM D-792 | |
| 成型收縮率 (2mm(t)) | 1.2-1.6 | % | SGC Method |
| 屈服拉伸強度 (50mm/min) | 27 | MPa | ASTM D-638 |
| 斷裂伸長率 (50mm/min) | 150 | % | ASTM D-638 |
| 彎曲強度 | 33 | MPa | ASTM D-747 |
| 彎曲模量 | 1196 | MPa | ASTM D-790 |
| IZOD沖擊強度 (23℃) | 11 | kg·cm/cm | ASTM D-256 |
| 洛氏硬度 (23℃) | 85 | R scale | ASTM D-785 |
| 熱變形溫度 (4.6kg/cm(1/4")) | 100 | ℃ | ASTM D-648 |
| 阻燃性 | UL 94 | ||
| (1/8") | V-2 | ||
| (1/16") | V-2 | ||
| (1/32") | V-2 |