| 熔體流動(dòng)速率 (230℃,2.16kg) | 8 | g/10min | ASTM D-1238 |
| 密度 | 0.91 | g/cm | ASTM D-1505 |
| 模具收縮率 (2mm(t)) | 1.5-1.8 | % |
| 抗張強(qiáng)度(屈服) (50mm/min) | 360 | kg/cm | ASTM D-638 |
| IZOD沖擊強(qiáng)度 (1/4",23℃) | 3 | kg·cm/cm | ASTM D-256 |
| 彎曲模量 | 16000 | kg/cm | ASTM D-790 |
| 洛氏硬度 (23℃) | 100 | R scale | ASTM D-785 |
| 斷裂伸長(zhǎng)率 (50mm/min) | 500 | % | ASTM D-638 |
| 抗張強(qiáng)度(斷裂) (50mm/min) | 250 | kg/cm | ASTM D-638 |
| 熔點(diǎn) (SGC) | 161 | DSC | |
| 可燃性 (1/8") | HB | UL 94 | |
| 熱變形溫度 | ASTM D-648 | ||
| (18.6kg/cm(1/8")) | 65 | ℃ | |
| (4.6kg/cm(1/8) | 155 | ℃ | |
| 維卡軟化點(diǎn) (1kg) | 155 | ASTM D-1525 | |
| 可燃性 (1/16") | HB | UL 94 |