| 熔體流動(dòng)速率 (230℃,2.16kg) | 7 | g/10min | ASTM D-1238 |
| 密度 | 0.9 | g/cm | ASTM D-1505 |
| 模具收縮率 (2mm(t)) | 1.5-1.8 | % |
| 抗張強(qiáng)度(屈服) (50mm/min) | 340 | kg/cm | ASTM D-638 |
| 抗張強(qiáng)度(斷裂) | 350 | ||
| 洛氏硬度 (23℃) | 90 | R scale | ASTM D-785 |
| 彎曲模量 | 10000 | kg/cm | ASTM D-790 |
| 斷裂伸長(zhǎng)率 | >500 | % | |
| IZOD沖擊強(qiáng)度 (1/4",-20℃) | 3 | kg·cm/cm | ASTM D-256 |
| 維卡軟化點(diǎn) (1kg) | 130 | ℃ | ASTM D-1525 |
| 熱變形溫度 (4.6kg/cm(1/8")) | 95 | ℃ | ASTM D-648 |
| 熔點(diǎn) (DSC) | 142 | ℃ | SGC |