| 規(guī)格級別 | 注塑 其它 增韌 | 外觀顏色 | |
| 該料用途 | 用于必須要有超強韌性的高負(fù)載零件。 | ||
| 備注說明 | 加工特性：高黏度樹脂，適合較易充填之模具。表面經(jīng)潤滑。產(chǎn)品特性：超強韌性聚甲醛樹脂。 | ||
| 加工條件 |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 模收縮 | 1.2-1.4 | % | ||
| 比重 | ASTM D-792 | 1.34 | |||
| 自燃性 | UL-94 | HB | |||
| 吸水量 | 50%相對濕度 | ASTM D-570 | 0.35 | % | |
| 吸水量 | 24小時浸漬 | ASTM D-570 | 0.43 | % | |
| 吸水量 | 浸漬平衡點 | ASTM D-570 | 0.85 | % | |
| 機械性能 | 拉伸強度 | 100℃ | ASTM D-638 | >17 | MPa |
| 拉伸強度 | -55℃ | ASTM D-638 | 99 | MPa | |
| IZOD沖擊試驗 | 缺口-40℃ | ASTM D-256 | 249 | j/m | |
| 撓曲系數(shù) | 100℃ | ASTM D-790 | 340 | MPa | |
| 破裂點拉伸變形量 | 122℃ | ASTM D-638 | >480 | % | |
| 洛氏硬度M | ASTM D-785 | 58 | |||
| 抗拉伸沖擊強度 | 長試片23℃ | ASTM D-1822 | 1590 | kj/m2 | |
| 壓縮應(yīng)力 | 23℃,10%變形 | ASTM D-695 | 52 | MPa | |
| 洛氏硬度R | ASTM D-785 | 105 | |||
| 撓曲系數(shù) | -55℃ | ASTM D-790 | 3260 | MPa | |
| 拉伸強度 | 70℃ | ASTM D-638 | >29 | MPa | |
| 破裂點拉伸變形量 | 100℃ | ASTM D-638 | >580 | % | |
| 撓曲系數(shù) | 122℃ | ASTM D-790 | 230 | MPa | |
| 破裂點拉伸變形量 | 70℃ | ASTM D-638 | >498 | % | |
| 破裂點拉伸變形量 | -55℃ | ASTM D-638 | 455 | % | |
| IZOD沖擊試驗 | 23℃ | ASTM D-256 | 901 | j/m | |
| 抗剪強度 | 23℃ | ASTM D-732 | 34 | MPa | |
| 破裂點拉伸變形量 | 23℃ | ASTM D-638 | 521 | % | |
| 撓曲系數(shù) | 23℃ | ASTM D-790 | 1280 | MPa | |
| 撓曲系數(shù) | 70℃ | ASTM D-790 | 650 | MPa | |
| 壓縮應(yīng)力 | 23℃,1%變形 | ASTM D-695 | 8 | MPa | |
| 撓曲變形強度 | 23℃ | ASTM D-790 | 40 | MPa | |
| 撓曲疲勞忍耐限度 | 50%RH,23℃,106周期 | ASTM D-671 | 16 | MPa | |
| 拉伸強度 | 23℃ | ASTM D-638 | 64 | MPa | |
| 彈性系數(shù) | 23℃ | ASTM D-638 | 1280 | MPa | |
| 拉伸強度 | 122℃ | ASTM D-638 | >11 | MPa | |
| 負(fù)載變形量 | 140kg/cm2,50℃ | ASTM D-621 | 3.0 | % | |
| 電氣性能 | 容積電阻率 | 23℃,0.2%含水量 | ASTM D-257 | 2.3×1014 | Ω.cm |
| 介電因數(shù) | 50%RH,23℃,106Hz | ASTM D-150 | 0.007 | ||
| 抗電弧 | 3.1mm | ASTM D-495 | 120 | sec | |
| 介電強度 | 瞬間Short time(2.3mm) | ASTM D-149 | 19.9(2.3) | kv/mm | |
| 介電常數(shù) | 50%RH,23℃,102～106Hz | ASTM D-150 | 4.1 | Ω.cm | |
| 熱性能 | 熱畸變溫度 | 0.5MPa | ASTM D-648 | 168 | ℃ |
| 熱畸變溫度 | 1.8MPa | ASTM D-648 | 65 | ℃ | |
| 線性熱膨脹系數(shù) | 104～160℃ | ASTM D-696 | 12.8 | 10-5m/m℃ | |
| 線性熱膨脹系數(shù) | -40～29℃ | ASTM D-696 | 9.9 | 10-5m/m℃ | |
| 線性熱膨脹系數(shù) | 60～104℃ | ASTM D-696 | 9.7 | 10-5m/m℃ | |
| 線性熱膨脹系數(shù) | 29～60℃ | ASTM D-696 | 10.6 | 10-5m/m℃ | |
| 熔點 | ASTM D-2133 | 175 | ℃ | ||