| 規(guī)格級別 | 擠出 其它 其它 | 外觀顏色 | |
| 該料用途 | |||
| 備注說明 | 特性：高粘度 | ||
| 加工條件 |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 10.7 | % | |
| 成型收縮率 | UBEb | 1.2 | % | ||
| 吸水率 | ASTM D-570 | 1.8 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.14 | ||
| 薄霧 | 3 | % | |||
| 光澤 | 140 | % | |||
| 薄膜厚度 | 50 | µm | |||
| 靜態(tài)磨擦 | 1.0 | ||||
| 機械性能 | 彎曲強度 | 23° | ASTM D-790 | 400 | kgf/cm2 |
| 彎曲彈性率 | 80° | ASTM D-790 | 7000 | kgf/cm2 | |
| 屈服下的伸張強度 | -30° | ASTM D-638 | 1100 | kgf/cm2 | |
| 斷裂下的延伸率 | 23° | ASTM D-638 | >200 | % | |
| 屈服下的伸張強度 | 200 | kgf/cm2 | |||
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 55 | ||
| 彎曲強度 | 80° | ASTM D-790 | 250 | kgf/cm2 | |
| 彎曲彈性率 | 23° | ASTM D-790 | 25000 | kgf/cm2 | |
| TABER磨耗率 | ASTM D-1044 | 7 | mg | ||
| 屈服下的伸張強度 | 80° | ASTM D-638 | 320 | kgf/cm2 | |
| 彎曲強度 | -30° | ASTM D-790 | 1400 | kgf/cm2 | |
| 斷裂下的伸張強度 | 23° | ASTM D-638 | >720 | kgf/cm2 | |
| 1%變形下的壓縮強度 | 23° | ASTM D-695 | 200 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 85 | ||
| 1%變形下的壓縮強度 | 23° | ASTM D-695 | 100 | kgf/cm2 | |
| 屈服下的伸張強度 | 80° | ASTM D-638 | 180 | kgf/cm2 | |
| 模壓力 | 4700 | kgf/cm2 | |||
| 抗沖擊強度 | -30° | ASTM D-256 | 5.0 | kgf.cm/cm | |
| 彎曲強度 | -30° | ASTM D-790 | 1300 | kgf/cm2 | |
| 擠剪強度 | 23° | ASTM D-732 | 650 | kgf/cm2 | |
| 屈服下的伸張強度 | -30° | ASTM D-638 | 870 | kgf/cm2 | |
| 彎曲強度 | 23° | ASTM D-790 | 1100 | kgf/cm2 | |
| 彎曲強度 | 80° | ASTM D-790 | 400 | kgf/cm2 | |
| 屈服下的伸張強度 | 23° | ASTM D-638 | 750 | kgf/cm2 | |
| 屈服下的延伸率 | 23° | ASTM D-638 | 8 | % | |
| 彎曲彈性率 | -30° | ASTM D-790 | 33000 | kgf/cm2 | |
| 屈服下的伸張強度 | 23° | ASTM D-638 | 400 | kgf/cm2 | |
| 彎曲彈性率 | 23° | ASTM D-790 | 7000 | kgf/cm2 | |
| 抗沖擊強度 | 23° | ASTM D-256 | 50 | kgf.cm/cm | |
| 抗沖擊強度 | 23° | ASTM D-256 | 7.5 | kgf.cm/cm | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 85 | ||
| 斷裂下的伸張強度 | 780 | kgf/cm2 | |||
| 彎曲彈性率 | 80° | ASTM D-790 | 4000 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 120 | ||
| 擠剪強度 | 23° | ASTM D-732 | 600 | kgf/cm2 | |
| 彎曲彈性率 | -30° | ASTM D-790 | 35000 | kgf/cm2 | |
| 斷裂下的伸張率 | 620 | % | |||
| 電氣性能 | 介電損耗 | 60HZ | ASTM D-150 | 0.01 | |
| 絕緣耐力 | ASTM D-149 | 20 | KV/mm | ||
| 介電常數(shù) | 106HZ | ASTM D-150 | 3.5 | ||
| 介電損耗 | 106HZ | ASTM D-150 | 0.12 | ||
| 介電損耗 | 103HZ | ASTM D-150 | 0.10 | ||
| 體積電阻率 | ASTM D-257 | 1012 | Ω.cm | ||
| 介電損耗 | 106HZ | ASTM D-150 | 0.02 | ||
| 介電常數(shù) | 106HZ | ASTM D-150 | 4.5 | ||
| 體積電阻率 | ASTM D-257 | 1015 | Ω.cm | ||
| 介電常數(shù) | 103HZ | ASTM D-150 | 8.0 | ||
| 介電常數(shù) | 60HZ | ASTM D-150 | 3.9 | ||
| 介電損耗 | 60HZ | ASTM D-150 | 0.10 | ||
| 介電常數(shù) | 60HZ | ASTM D-150 | 9.0 | ||
| 介電常數(shù) | 103HZ | ASTM D-150 | 3.8 | ||
| 介電損耗 | 103HZ | ASTM D-150 | 0.02 | ||
| 熱性能 | 熔點 | DSC | 215-225 | °C | |
| 線性熱膨脹系數(shù) | ASTM D-696 | 8 | X的10-5cm/cm/°C | ||
| 燃燒率 | UL94 | V-2 | |||
| 熱變形溫度 | 18.6kgf/cm2 | ASTM D-648 | 65 | °C | |
| 熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 170 | °C | |
| 其它性能 | 氧氣 | 25 | me/m2.24h | ||