| 分類: | E11018-M, SFA/AWS A5.5, E 69 5 Mn2NiMo B 32 H5, EN ISO 18275-A |
| 認(rèn)證: | AWS, E11018-M, ABS, 4Y62 H5, BV, EN 13479, CE, 4Y62 H5, DNV, 4Y62 H5, LR, (N) Q1N, HY80, MoD, UNA 272581, Seproz |
Approvals are based on factory b. Please contact ESAB for more inbation.
| Alloy Type: | C, Mn, 2%Ni, 0.4%Mo |
| Coating Type: | Basic |
| Diffusible Hydrogen: | < 5.0 ml/100g |
| Welding Current: | AC, DC+- |
| Impact Value | Testing Temperature |
| ISO As welded | |
| 80 J | -50 °C |
| AWS As welded | |
| - | -50 °C |
| Elongation | Tensile Strength | Yield Strength |
| ISO As welded | ||
| 22 % | 800 MPa | 740 MPa |
| AWS As welded | ||
| - | - | - |
| Fusion time per electrode at 90% I max | kg weld bl/kg electrodes | Number of electrodes/kg weld bl | 安培 | 熔敷率 | 電壓 V | 直徑 |
| 46.6 hr | 0.61 kg | 83.3 | 55-105 A | 0.93 kg/h | 25.3 V | 2.5 x 350 mm |
| 64.3 hr | 0.56 kg | 46.2 | 90-140 A | 1.21 kg/h | 22.8 V | 3.2 x 350 mm |
| 90.0 hr | 0.61 kg | 23.1 | 110-180 A | 1.72 kg/h | 22.8 V | 4.0 x 450 mm |
| 90.3 hr | 0.63 kg | 13.5 | 190-280 A | 2.75 kg/h | 24.6 V |
5.0 x 450 mm |