東莞市廣業(yè)塑膠原料有限公司銷售tpv 101-64 以下是關(guān)于tpv 101-64原料的一些知識介紹,供商友間學(xué)習(xí)探討,更多相關(guān)資訊可來電咨詢(13412886878鄧生):
一、tpv 101-64微球發(fā)泡TPV復(fù)合材料制備及其性能:
The hot air aging results of 110℃×1 000hand 135℃×168hindicated that the microsphere foamed TPV composites had excellent heat aging properties.The hardness change was only 2,the tensile strength retention rate was as high as 93.5%and 95.7%,and the elongation at break retention was 80.8%and 85.9%,respectively compared with the TPV perbance before aging.The dimensional shrinkages of the microsphere foamed TPV composites in the Ldirection and the Tdirection after aging were less than 1.0%.SEM of quenching section studies showed that when the screw rotation speed was 160r/min,the microbubble bing agent had larger cell size and unib distribution,and the compatibility between the expanded microsphere foaming agent and the substrate TPV was better,and the micro-foamed TPV composite material had a superior extrusion appearance and comprehensive physical and mechanical properties.
Key words:microsphere foaming agent;TPV;thermoplastic elastomer;hot air aging
?
二、tpv 101-64廢舊輪胎橡膠粉填充改性TPV的研究:
Study on Filling and Modified TPV of Waste Tire Rubber Powder
LV Huai - xing TU Zhong – dan (GEM Co. , Ltd , Shenzhen Guangdong 518101 , China )
【Abstract】The TPV /WGRT thermoplastic elastomer was prepared on an internal mixer , and the effect of the amount of WGRT added and the amount of additives added on the perbance of the matrix was investigated . The results showed that when WGRT was added separaby , the tensile strength and modulus at 100% elongation of the matrix decreased gradually with the increasing of the addition amount , and the Shore A hardness gradually increased . When the addition amount of M603 compatibilizer increased , the tensile strength and modulus at 100% elongation of the matrix increased gradually , and then tend to be stable under adding different amounts of WGRT.
?
三、關(guān)于廣業(yè)tpv 101-64:廣業(yè)塑膠原料有限公司以客戶為根本,堅持走正品、高品質(zhì)、優(yōu)服務(wù)路線。積累了業(yè)界良好口碑,客戶遍及大江南北是生產(chǎn)廠家合作的最佳之選。美國??松梨诠舅兄粕a(chǎn)的彈性體TPV系列以性能穩(wěn)定,質(zhì)量上乘而深受廣大生產(chǎn)廠家青睞。我公司常年經(jīng)銷批發(fā)埃克森美孚山都坪系列TPV,歡迎來電咨詢合作。
?
四、tpv 101-64 圖片展示:
五、tpv 101-64環(huán)烷油填充EPDM/PP TPV的性能研究:
其次考察環(huán)烷油含量對EPDM/PP TPV 性能的影響,圖1 為環(huán)烷油充油量對EPDM/PPTPV熔體流動速率的影響?由圖1可以看出,隨著充油量的不斷增加,EPDM/PPTPV的MFR從整體上來看也呈現(xiàn)了不斷增加的趨勢?當(dāng)充油質(zhì)量分?jǐn)?shù)低于20%時,TPV的MFR增長幅度緩慢且平穩(wěn),MFR數(shù)值基本維持在1.5左右;當(dāng)TPV中充油質(zhì)量分?jǐn)?shù)超過25%的時候,其MFR出現(xiàn)了大幅度升高的現(xiàn)象,當(dāng)充油質(zhì)量分?jǐn)?shù)達(dá)到40%的時候,MFR大幅度增加,達(dá)到5.7g/10min?
?
六、tpv 101-64無鹵阻燃劑對TPV性能的影響:
結(jié)論:1)隨著無鹵阻燃劑用量的增加,材料的硬度和壓縮永久形變呈現(xiàn)先減小然后增加的變化趨勢,其原因與無機(jī)填料的硬化效應(yīng)和分散劑的軟化效應(yīng)有關(guān)。2)隨著阻燃劑用量的增加,拉伸強(qiáng)度和100%定伸強(qiáng)度降低,斷裂伸長率降低。3)隨著剪切速率的增加,材料的表觀黏度降低,呈現(xiàn)剪切變稀現(xiàn)象,添加25% 阻燃劑的黏度較純TPV略有降低,超過35%后黏度增加。4)當(dāng)阻燃劑用量≥35% 時,1.6 mm可達(dá)到V一1,3.2 mm可達(dá)到V-(),具有較好的防吸水性能,能滿足建材和電線電纜行業(yè)的要求。
?
七、tpv 101-64采購聯(lián)系方式:
聯(lián)系地址:廣東省東莞市樟木頭塑膠原料市場一期
聯(lián)系電話/微信:13412886878(鄧生)
傳真號碼:0769-82933089
騰訊 QQ:673160582
?
八、廣業(yè)視角-- 4月24日PET漲跌觀點?? tpv 101-64
04月24日訊
??商品名稱:PET
??最新價格(4月124日):8662.50元/噸
??分析要點:原料PTA行情窄幅震蕩,同時原料乙二醇價格疲軟下跌,PET成本端支撐面一般。國內(nèi)PET庫存處于低位,暫無銷售壓力,廠家長遠(yuǎn)期訂單讓利可談。但近期下游采購商觀望態(tài)度為主,實際成交量不高,市場交易氛圍清淡。致使國內(nèi)PET價格疲軟下跌,預(yù)計短期內(nèi)國內(nèi)PET瓶級廠家主流報價范圍8500-8700元/噸。
??后市預(yù)測:后市行情或?qū)⒊掷m(xù)疲軟運(yùn)行。