LNP? LUBRICOMP? LL003 compound
聚醚醚酮
SABIC Innovative Plastics
產品說明:
LNP LUBRICOMP LL003 is a compond based on Polyetheretherketone resin containing 15% PTFE Lubricant. Added feature of this material is: Wear Resistant.
Also known as: LNP* LUBRICOMP* Compound LL-4030
Product reorder name: LL003
|
添加劑 |
· PTFE潤滑劑 (15%) |
|||
|
特性 |
|
|||
|
加工方法 |
· 注射成型 |
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|
比重 |
|
|
ASTM D792 |
|
-- |
1.39 |
|
|
|
-- |
1.39 |
g/cm3 |
|
|
收縮率 |
|
|
ASTM D955 |
|
流動 : 24小時 |
9.0E-3 到 0.020 |
in/in |
|
|
橫向流動 : 24小時 |
0.010 到 0.030 |
in/in |
|
|
吸水率 |
|
|
|
|
24 hr, 50% RH |
0.078 |
% |
ASTM D570 |
|
平衡, 73°F, 50% RH |
0.089 |
% |
ISO 62 |
|
機械性能 |
額定值 |
單位制 |
測試方法 |
|
拉伸模量 |
|
|
|
|
-- 2 |
436000 |
psi |
ASTM D638 |
|
-- |
446000 |
psi |
ISO 527-2/1 |
|
抗張強度 |
|
|
|
|
屈服 3 |
9340 |
psi |
ASTM D638 |
|
屈服 |
8990 |
psi |
ISO 527-2/5 |
|
斷裂 3 |
9340 |
psi |
ASTM D638 |
|
斷裂 |
8990 |
psi |
ISO 527-2/5 |
|
伸長率 |
|
|
|
|
屈服 3 |
4.6 |
% |
ASTM D638 |
|
屈服 |
3.3 |
% |
ISO 527-2/5 |
|
斷裂 3 |
4.6 |
% |
ASTM D638 |
|
斷裂 |
|
|
|