LNP? LUBRICOMP? 9X06483 compound
聚酰胺 46
產(chǎn)品說(shuō)明：
LNP*
LUBRICOMP* 9X06483 is a compound based on a Nylon 4/6 containing PTFE. Added
features of this grade are: Heat Stabilized, Wear Resistant.
Also known as: LNP* LUBRICOMP* Compound STN-L-4030 HS
Product reorder name: 9X06483LNP?
LUBRICOMP? 9X06483 compound 物性表
|
基本信息 |
|
|
添加劑 |
· PTFE潤(rùn)滑劑 · 熱穩(wěn)定劑 |
|
特性 |
· 耐磨損性良好 · 熱穩(wěn)定性 · 潤(rùn)滑 |
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
比重 |
|
|
|
|
-- |
1.29 |
g/cm3 |
ASTM D792 |
|
-- |
1.28 |
g/cm3 |
ISO 1183 |
|
收縮率 |
|
|
ASTM D955 |
|
流動(dòng) : 24小時(shí) |
1.0 到 3.0 |
% |
ASTM D955 |
|
橫向流動(dòng) : 24小時(shí) |
2.0 到 4.0 |
% |
ASTM D955 |
|
吸水率 |
|
|
|
|
24 hr, 50% RH |
1.8 |
% |
ASTM D570 |
|
平衡, 23°C, 50% RH |
2.7 |
% |
ISO 62 |
|
機(jī)械性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
拉伸模量 |
|
|
|
|
-- 1 |
3130 |
MPa |
ASTM D638 |
|
-- |
3010 |
MPa |
ISO 527-2/1 |
|
抗張強(qiáng)度 |
|
|
|
|
屈服 2 |
80.0 |
MPa |
ASTM D638 |
|
屈服 |
78.0 |
MPa |
ISO 527-2/5 |
|
斷裂 3 |
74.0 |
MPa |
ASTM D638 |
|
斷裂 |
76.0 |
MPa |
ISO 527-2/5 |
|
伸長(zhǎng)率 |
|
|
|
|
屈服 4 |
5.8 |
% |
ASTM D638 |
|
屈服 |
6.5 |
% |
ISO 527-2/5 |
|
斷裂 5 |
5.9 |
% |
ASTM D638 |
|
斷裂 |
6.6 |
% |
ISO 527-2/5 |
|
彎曲模量 |
|
|
|
|
50.0 mm 跨距 6 |
2960 |
MPa |
ASTM D790 |
|
-- 7 |
2800 |
MPa |
ISO 178 |
|
彎曲應(yīng)力 |
101 |
MPa |
ISO 178 |
|
摩擦系數(shù) |
|
|
ASTM D3702 Modified |
|
與自身 - 動(dòng)態(tài) |
0.32 |
|
ASTM D3702 Modified |
|
與自身 - 靜態(tài) |
0.32 |
|
ASTM D3702 Modified |
|
磨損因數(shù) |
|
|
ASTM D3702 Modified |
|
Ring |
-0.0500 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
|
Washer |
11.5 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
|
沖擊性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
懸壁梁缺口沖擊強(qiáng)度 |
|
|
|
|
23°C |
52 |
J/m |
ASTM D256 |
|
23°C 8 |
5.0 |
kJ/m2 |
ISO 180/1A |
|
無(wú)缺口懸臂梁沖擊 |
|
|
|
|
23°C |
920 |
J/m |
ASTM D4812 |
|
23°C 9 |
56 |
kJ/m2 |
ISO 180/1U |
|
裝有測(cè)量?jī)x表的落鏢沖擊 |
|
|
|
|
23°C, Total Energy |
3.60 |
J |
ASTM D3763 |
|
-- |
0.800 |
J |
ISO 6603-2 |
|
熱性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
載荷下熱變形溫度 |
|
|
|
|
0.45 MPa, 未退火, 3.20 mm |
283 |
°C |
ASTM D648 |
|
0.45 MPa, 未退火, 64.0 mm 跨距 10 |
276 |
°C |
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm |
151 |
°C |
ASTM D648 |
|
1.8 MPa, 未退火, 64.0 mm 跨距 11 |
92.0 |
°C |
ISO 75-2/Af |