Plexar® PX1007
乙烯醋酸乙烯共聚物
LyondellBasell Industries
產(chǎn)品說明:
Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, bl, and paperboard. Product grades primarily used for blown and cast films, sheet and thermobing, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet b. Contact your Plexar sales and/or Equistar technical service representative for more inbation and specific recommendations for your application(s).
|
用途 |
|
|||
|
機構(gòu)評級 |
|
|||
|
形式 |
|
|||
|
加工方法 |
|
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|
密度 |
0.931 |
g/cm3 |
ASTM D1505 |
|
熔流率（熔體流動速率） (190°C/2.16 kg) |
3.1 |
g/10 min |
ASTM D1238 |
|
薄膜 |
額定值 |
單位制 |
測試方法 |
|
薄膜厚度 - 經(jīng)測試 |
2.0 |
mil |
|
|
抗張強度 |
|
|
ASTM D882 |
|
MD : 屈服, 2.0 mil, 吹塑薄膜 |
1840 |
psi |
|
|
TD : 屈服, 2.0 mil, 吹塑薄膜 |
1040 |
psi |
|
|
MD : 斷裂, 2.0 mil, 吹塑薄膜 |
3630 |
psi |
|
|
TD : 斷裂, 2.0 mil, 吹塑薄膜 |
3230 |
psi |
|
|
伸長率 |
|
|
ASTM D882 |
|
MD : 屈服, 2.0 mil, 吹塑薄膜 |
62 |
% |
|
|
TD : 屈服, 2.0 mil, 吹塑薄膜 |
64 |
% |
|
|
MD : 斷裂, 2.0 mil |
380 |
% |
|
|
TD : 斷裂, 2.0 mil, 吹塑薄膜 |
650 |
% |
|
|
埃爾曼多夫抗撕強度 |
|
|
ASTM D1922 |
|
MD : 2.0 mil, 吹塑薄膜 |
290 |
g |
|
|
TD : 2.0 mil, 吹塑薄膜 |
230 |
g |
|
|
水氣透過率 (100% RH, 2.0 mil, 吹塑薄膜) |
|
|
|