類別
|
品名
|
AWS型號(hào)
|
熔敷金屬化學(xué)成分(%)
|
熔敷金屬力學(xué)性能
|
|||||||||||
σ0.2(MPa)
|
δb(MPa)
|
δ(%)
|
|||||||||||||
C
|
Mn
|
Si
|
Cr
|
Ni
|
Mo
|
Nb
|
Cu
|
N
|
|||||||
不銹鋼電焊條
|
ASpezial
|
E318-15
|
≤0.07
|
1.3
|
<0.5
|
19.0
|
12.0
|
2.8
|
>10×C
|
390
|
600
|
30
|
|||
AW
|
E318-17
|
<0.03
|
0.8
|
<0.9
|
19.0
|
12.0
|
2.8
|
>10×C
|
390
|
600
|
30
|
||||
ATS4
|
E308H-15
|
0.05
|
1.6
|
0.3
|
18.5
|
9.5
|
350
|
550
|
35
|
||||||
C
|
E310-15
|
0.13
|
2.5
|
1.0
|
25.0
|
20.0
|
350
|
550
|
25
|
||||||
CW310-16
|
E310-16
|
0.10
|
2.0
|
0.5
|
26.0
|
21.0
|
380
|
570
|
35
|
||||||
CM
|
E310-15
|
0.12
|
4.5
|
1.0
|
25.0
|
20.0
|
380
|
550
|
30
|
||||||
CR
|
E310H-15
|
0.40
|
2.5
|
1.0
|
25.5
|
21.5
|
400
|
600
|
10
|
||||||
D
|
E309-15
|
0.11
|
0.9
|
1.0
|
22.5
|
11.0
|
350
|
550
|
30
|
||||||
DW
|
E309-17
|
0.11
|
0.8
|
0.9
|
22.5
|
12.5
|
350
|
550
|
30
|
||||||
GESpezial
|
E316L-15
|
≤0.04
|
1.3
|
0.2
|
18.5
|
11.5
|
2.8
|
350
|
580
|
35
|
|||||
GEW/F(向下立焊)
|
E316L-16
|
0.02
|
0.8
|
0.7
|
18.5
|
11.5
|
2.6
|
350
|
580
|
30
|
|||||
GEW316L-17
|
E316L-17
|
≤0.04
|
0.8
|
<0.9
|
19.0
|
12.5
|
2.8
|
350
|
580
|
35
|
|||||
HESpezial
|
E347-15
|
≤0.03
|
1.3
|
0.5
|
19.5
|
10.0
|
>13×C
|
390
|
550
|
30
|
|||||
HW
|
E347-17
|
<0.07
|
0.8
|
<0.9
|
19.5
|
10.0
|
>10×C
|
380
|
550
|
30
|
|||||
JESpezial
|
E308L-15
|
≤0.04
|
1.0
|
0.3
|
19.5
|
10.0
|
350
|
550
|
35
|
||||||
JEW308L-17
|
E308L-17
|
<0.04
|
0.8
|
<0.9
|
19.5
|
9.5
|
350
|
550
|
35
|
||||||
X
|
E307-15
|
0.10
|
7.0
|
0.6
|
18.5
|
8.0
|
0.12
|
390
|
620
|
35
|
|||||
XW
|
E307-16
|
0.10
|
7.0
|
0.6
|
18.5
|
8.0
|
0.08
|
390
|
620
|
35
|
|||||
13/04
|
E410NiMo-15
|
0.04
|
0.5
|
<0.4
|
12.0
|
4.5
|
0.5
|
620
|
830
|
15
|
|||||
14K
|
E410-15
|
0.06
|
0.5
|
<0.4
|
12.5
|
1.3
|
450
|
650
|
15
|
||||||
14KSo
|
E410-15
|
0.06
|
0.5
|
<0.4
|
12.0
|
1.1
|
450
|
650
|
20
|
||||||
16/36
|
E330-15
|
0.22
|
1.3
|
<0.5
|
18.5
|
35.0
|
2.3
|
320
|
550
|
15
|
|||||
17
|
E430-15
|
0.06
|
0.5
|
0.5
|
17.0
|
<0.6
|
340
|
530
|
20
|
||||||
1720
|
E430-15
|
0.18
|
0.40
|
≤0.5
|
16.0
|
0.50
|
1.10
|
||||||||