| PA66 CM3006 日本東麗工業(yè)株式會社 物性數(shù)據(jù) |
| 規(guī)格級別： | --- | 外觀顏色： | --- |
| 用途概述： | --- | ||
| 備注說明： | 類型：尼龍-66未強化 | ||
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 |
|
數(shù)據(jù)單位 | |||||
| 基本性能 | 吸水率 | 23℃ | ASTM D-570 |
|
% | ||||
| 物理性能 | 比重 | --- | ASTM D-792 |
|
--- | ||||
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 |
|
mg/1000次 | |||||
| 機械性能 | IZOD沖擊強度 | 23℃，無缺口1/2 | --- |
|
kg.cm/cm | ||||
| IZOD沖擊強度 | 23℃，無缺口1/8 | --- |
|
kg.cm/cm | |||||
| 洛氏硬度 | 23℃ | ASTM D-785 |
|
R | |||||
| 洛氏硬度 | 23℃ | ASTM D-785 |
|
--- | |||||
| 抗拉屈服強度 | -40℃ | ASTM D-638 |
|
Kg/cm2 | |||||
| 抗拉屈服強度 | 23℃ | ASTM D-638 |
|
Kg/cm2 | |||||
| 抗拉屈服強度 | 80℃ | ASTM D-638 |
|
Kg/cm2 | |||||
| 抗拉斷裂強度 | 23℃ | ASTM D-638 |
|
Kg/cm2 | |||||
| 斷裂伸長率 | 23℃ | ASTM D-638 |
|
% | |||||
| 撓曲強度 | -40℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 撓曲強度 | 23℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 撓曲強度 | 80℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 撓曲��量 | -40℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 撓曲模量 | 23℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 撓曲模量 | 80℃ | ASTM D-790 |
|
Kg/cm2 | |||||
| 壓縮強度 | 23℃ | ASTM D-695 |
|
Kg/cm2 | |||||
| 抗剪強度 | 23℃ | ASTM D-732 |
|
Kg/cm2 | |||||
| IZOD沖擊強度 | -40℃，無缺口1/2 | --- |
|
kg.cm/cm | |||||
| 電氣性能 | 體積電阻率 | --- | ASTM D-257 |
|
Ω.cm | ||||
| 介電常數(shù) | 50HZ | ASTM D-150 |
|
--- | |||||
| 損耗因素 | 50Hz | ASTM D-150 |
|
--- | |||||
| IEC導(dǎo)電徑蹤指數(shù) | --- | UL 746 |
|
V | |||||
| 熱 性 能 | UL-94抗燃級 | 1/16" | UL 94 |
|
--- | ||||
| 線性熱膨脹系數(shù) | --- | ASTM D-696 |
|
10-5cm/cm | |||||
| 熱撓曲溫度 | 4.6kg/cm2 | ASTM D-648 |
|
℃ | |||||
| 熔點 | --- | 差示掃描測熱計DSC法 |
|
℃ | |||||
| 比熱 | --- | --- |
|
Cal/g.°C | |||||
| 導(dǎo)熱系數(shù) | --- | --- |
|
Kcal/m.hr.°C | |||||